I did it similar in the past with epoxy filler on my hard tanks - its work. 

vbr Carsten

"Alan James" <alanjames@xtra.co.nz> schrieb:
> Hi Glen,
> This solution is untried & open to criticism, but you could make up a thick paste of colloidal silica
> & epoxy & smear it over the ct ring then put a mold release agent on the hatch ring. Maybe fill the
> O-ring grove with Vaseline & close the hatch tight for 12 hours. You'll be left with a few small voids
> that need tidying up including the o-ring grove. Might be a problem if you have a half dovetail grove.
> Would try it on two bits of steel first in case they don't come apart.
> Regards Alan
>   ----- Original Message ----- 
>   From: Glen Brown 
>   To: personal_submersibles@psubs.org 
>   Sent: Friday, March 11, 2011 3:49 AM
>   Subject: Re: [PSUBS-MAILIST] CT ring surface not true.
> 
> 
>   Hi All
>   I need Idea's to get my ct ring surface to mate with my hatch ring as it has warped by + -  2mm in the welding
>   process.
>   Thanks Glen
> 




************************************************************************
************************************************************************
************************************************************************
The personal submersibles mailing list complies with the US Federal
CAN-SPAM Act of 2003.  Your email address appears in our database
because either you, or someone you know, requested you receive messages
from our organization.

If you want to be removed from this mailing list simply click on the
link below or send a blank email message to:
	removeme-personal_submersibles@psubs.org

Removal of your email address from this mailing list occurs by an
automated process and should be complete within five minutes of
our server receiving your request.

PSUBS.ORG
PO Box 53
Weare, NH  03281
603-529-1100
************************************************************************
************************************************************************
************************************************************************